Effect of structural defects on the magnetic properties of the EuBaCo1.90O5.36 single crystal

Abstract

The effect of structural defects in cobalt and oxygen sublattices with the constant average oxidation level 3+ of all cobalt ions on the magnetic properties of the EuBaCo_1.90O_5.36 single crystal has been studied. The magnetic properties of the single crystal and the polycrystalline sample of the corresponding composition are compared in the range T = 200–650 K. The results show that the cobalt-deficient EuBaCo_2–xO_5.5–δ samples demonstrate a three-dimensional XY ferromagnetic ordering of magnetic sublattices. The values of the effective magnetic moment at T > 480 K indicate the existence of the IS and HS states of Co³⁺ ions. The large difference of values of μ_eff of the EuBaCo_1.90O_5.36 single crystal and polycrystal can be due to that the magnetic ion spins lie in plane ab. The magnetic field directed along plane ab substantially influences the magnetic ordering at T < 300 K.