The Influence of Modification on Crystal Lattice Stability of Austenite in Stainless Steel

Using the methods of electron diffraction microscopy and X-ray diffraction analysis, the influence of alloying of the austenitic steel, Grade 110H13, with chromium and vanadium, as well as high-melting, ultrafine-grained TiO₂, ZrO₂ powders and Na₃AlF₆ cryolite on its structural-phase state and microstructure is investigated. It is shown that the matrix of non-modified steel is completely austenitic and consists of an iron-based solid solution and the interstitial (C, N, O and other) and substitutional (Cr, V and other) atoms simultaneously. Alloying with chromium and vanadium changes neither its phase composition nor defect structure, while alloy modification results in qualitatively new structural features: γ → ε-transformation, high-intensity microtwinning, defect structure changes, and a sharp increase in the scalar dislocation density. The features of the deformation-induced microtwinning and ε-martensite plates identified in the modified steel promote revealing additional microtwin systems in the matrix γ-phase, which result in structural changes making it possible to classify it as a γ′-phase. It is found out that an introduction of modifying additions gives rise to the following sequence of structural-phase transformations: γ→γ′→(γ′ +ε). The experimental data obtained demonstrate that as a result of modification the crystal lattice transits into a low-stability state. This transition is accompanied by marked structural-phase changes consisting in the formation of several microtwin systems and γ → ε-transformation. These structural-phase changes in the modified steel are due to the crystal-lattice transition into the low-stability state, followed by new structural-phase alterations.