Study of the high-coercivity material based on ε-Fe2O3 nanoparticles in the silica gel matrix

Аннотация

We report the results of investigations of ε-Fe₂O₃ magnetic nanoparticles obtained by incipient wetness impregnation of silica gel. It was established that the obtained samples with an iron content of 12‒16% mass % containing ε-Fe₂O₃ nanoparticles with an average size of 10 nm on the silica gel surface exhibit a room-temperature coercivity of about 10 kOe. Along with fabrication simplicity, this fact makes the prepared samples promising for application as a magnetically hard material.