Effect of gallium alloying on the structure, the phase composition, and the thermoelastic martensitic transformations in ternary Ni–Mn–Ga alloys

Аннотация

The effect of gallium alloying on the structure, the phase composition, and the properties of quasibinary Ni₅₀Mn_50–zGa_z (0 ⩽ z ⩽ 25 at %) alloys is studied over a wide temperature range. The influence of the alloy composition on the type of crystal structure in high-temperature austenite and martensite and the critical martensitic transformation temperatures is analyzed. A general phase diagram of the magnetic and structural transformations in the alloys is plotted. The temperature–concentration boundaries of the B2 and L2₁ superstructures in the austenite field, the tetragonal L1₀ (2M) martensite, and the 10M and 14M martensite phases with complex multilayer crystal lattices are found. The predominant morphology of martensite is shown to be determined by the hierarchy of the packets of thin coherent lamellae of nano- and submicrocrystalline crystals with planar habit plane boundaries close to {011}_B2. Martensite crystals are twinned along one of the 24 \(24\left\{ {011} \right\}{\left\langle {01\bar 1} \right\rangle _{B2}}\) “soft” twinning shear systems, which provides coherent accommodation of the martensitic transformation–induced elastic stresses.