Peculiarities of Phase Formation in TbBO3 during Isothermal Annealing

Аннотация

Detailed X-ray studies of changes in the structure of terbium orthoborate TbBO₃ in the course of successive high-temperature isothermal annealing of the initial mixture in the form of an amorphous precursor and in the form of a homogenized mixture of microcrystalline Tb₇O₁₂ and B₂O₃ powders have been carried out. It is shown that the formation of TbBO₃ crystals in both cases occurs through the formation of intermediate two-phase states. Particularly, the triclinic high-temperature ν-TbBO₃ phase is formed already at the first crystallization stages (about 600°C) almost simultaneously with the equilibrium vaterite modification of TbBO₃ (sp. gr. P63/mmc) during low-temperature annealing of an amorphous precursor, which transforms into the vaterite modification at an annealing temperature of 850°C. The phase of monoclinic terbium trioxoborate TbB₃O₆ is formed at the first stages of phase formation (about 800°C) almost simultaneously with the vaterite phase when the feedstock is annealed in the form of a homogenized mixture of microcrystalline Tb₇O₁₂ and B₂O₃ powders. It also transforms into the vaterite modification at an annealing temperature of 950°, which is preserved up to the highest annealing temperatures in the experiment (1200°C). A hypothetical explanation of the formation of such two-phase states during low-temperature annealing of the feedstock and their disappearance at higher annealing temperatures is proposed.