Low-Temperature Synthesis of Highly Dispersed Strontium Aluminate

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

A new method for producing highly dispersed strontium aluminate with specified properties (low bulk density, particle size and shape) is described. The essence of the method is the sequential multi-stage heat treatment of a concentrated water-carbohydrate solution of Al(NO3)3, Sr(NO3)2, and D-glucose. The final product has a molar ratio of SrO : Al2O3 = 1 : 1. The main stages of the synthesis have been characterized by X-ray powder diffraction, SEM, and TEM methods. The initial stages of crystallization of SrAl2O4 upon heating at 1400°C have been revealed.

Авторлар туралы

L. Kozlova

Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: kozzllova167@gmail.com
119991, Moscow, Russia

Yu. Ioni

Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences; Moscow Aviation Institute (National Research University)

Email: kozzllova167@gmail.com
119991, Moscow, Russia; 125993, Moscow, Russia

A. Son

Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: kozzllova167@gmail.com
119991, Moscow, Russia

G. Buzanov

Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Email: kozzllova167@gmail.com
119991, Moscow, Russia

G. Murav’eva

Moscow State University

Email: kozzllova167@gmail.com
119991, Moscow, Russia

I. Kozerozhets

Kurnakov Institute of General and Inorganic Chemistry, Russian Academy of Sciences

Хат алмасуға жауапты Автор.
Email: kozzllova167@gmail.com
119991, Moscow, Russia

Әдебиет тізімі

  1. Ptáček P., Šoukal F., Opravil T. et al. // Ceram. Int. 2014. V. 40. P. 9971. https://doi.org/10.1016/j.ceramint.2014.02.095
  2. Smets B.M.J. // Mater. Chem. Phys. 1987. V. 16. P. 283. https://doi.org/10.1016/0254-0584(87)90103-9
  3. Khattab T. A., Rehan M., Hamdy Y. et al. Ind. Eng. Chem. Res. 2018. V. 57. P. 11483. https://doi.org/10.1021/acs.iecr.8b01594
  4. Calatayud D.G., Jardiel T., Cordero-Oyonarte E. et al. // Int. J. Mol. Sci. 2022. V. 23. P. 3410. https://doi.org/10.3390/ijms23063410
  5. Madej D., Silarski M., Parzych S. // Mater. Chem. Phys. 2021. V. 260. 124095. https://doi.org/10.1016/j.matchemphys.2020.124095
  6. Clabau F., Rocquefelte X., Jobic S. et al. // Chem. Mater. 2005. V. 17. P. 3904. https://doi.org/10.1021/cm050763r
  7. Sharma S., James J., Gupta S. et al. // Materials. 2023. V. 16. № 236. https://doi.org/10.3390/ma16010236
  8. Tseng H., Tzou W., Wei S. et al. // J. Mater. Res. Technol. 2020. V. 9. P. 14051. https://doi.org/10.1016/j.jmrt.2020.10.003
  9. Terraschke H., Suta M., Adlung M. et al. // J. Spectrosc. (Hindawi). 2015. V. 2015. P. 1. https://doi.org/10.1155/2015/541958
  10. Li J., Wang J., Yu Y. et al. // J. Rare Earths. 2017. V. 35. P. 530. https://doi.org/10.1016/S1002-0721(17)60944-X
  11. Zhang Y., Li L., Zhang X. et al. // J. Rare Earths. 2008. V. 26. P. 656. https://doi.org/10.1016/S1002-0721(08)60156-8
  12. Jin Y., Long X., Zhu Y. et al. // J. Rare Earths. 2016. V. 34. P. 1206. https://doi.org/10.1016/S1002-0721(16)60155-2
  13. Chen L., Zhang Z., Tian Y. et al. // J. Rare Earths. 2017. V. 35. P. 127. https://doi.org/10.1016/S1002-0721(17)60890-1
  14. Zhao R., Pang R., Li H. et al. // J. Rare Earths. 2014. V. 32. P. 797. https://doi.org/10.1016/S1002-0721(14)60143-5
  15. Kumar A., Kedawat G., Kumar P. et al. // New J. Chem. 2015. V. 39. P. 3380. https://doi.org/10.1039/c4nj02333a
  16. Xu J., Tanabe S. // J. Lumin. 2019. V. 205. P. 581. https://doi.org/10.1016/j.jlumin.2018.09.047
  17. Castaing V., Arroyo E., Becerro A. et al. // J. Appl. Phys. 2021. V. 130. 080902. https://doi.org/10.1063/5.0053283
  18. Ayvacıklı M., Ege A., Yerci S. et al. // J. Lumin. 2011. V. 131. P. 2432. https://doi.org/10.1016/j.jlumin.2011.05.051
  19. Rojas-Hernandez R.E., Rodriguez M.A., Rubio-Marcos F. et al. // J. Mater. Chem. C. 2015. V. 3. P. 1268. https://doi.org/10.1039/c4tc02262a
  20. Kochergina T.A., Aleshkina S.S., Khudyakov M.M. et al. // Quantum Electron. 2018. V. 48. P. 733. https://doi.org/10.1070/QEL16740
  21. Kozerozhets I.V., Panasyuk G.P., Semenov E.A. et al. // Ceram. Int. 2022. V. 48. P. 7522. https://doi.org/10.1016/j.ceramint.2021.11.296
  22. Panasyuk G.P., Kozerozhets I.V., Semenov E.A. et al. // Inorg. Mater. 2019. V. 55. P. 929. https://doi.org/10.1134/S0020168519090139
  23. Бучинская И.И., Сорокин Н.И. // Журн. неорган. химии. 2023. Т. 68. № 7. С. 877.
  24. Solovieva A.Y., Ioni Y.V., Baskakov A.O. et al. // Russ. J. Inorg. Chem. 2017. V. 62. P. 711. https://doi.org/10.1134/S0036023617060225
  25. Tatumi S.H., Soares A. de F., Tudela D.R.G. et al. // Radiat. Phys. Chem. 2019. V. 157. P. 15. https://doi.org/10.1016/j.radphyschem.2018.12.013
  26. Steblevskaya N.I., Belobeletskaya M.V., Medkov M.A. et al. // Russ. J. Inorg. Chem. 2017. V. 62. P. 275. https://doi.org/10.1134/S0036023617030160
  27. Sera M., Yamamoto M., Tomita K. et al. // Chem. Phys. Lett. 2021. V. 780. 138916. https://doi.org/10.1016/j.cplett.2021.138916
  28. Kozerozhets I.V., Avdeeva V.V., Buzanov G.A. et al. // Inorganics. 2022. V. 10. № 11. P. 212. https://doi.org/10.3390/inorganics10110212
  29. Kozerozhets I.V., Panasyuk G.P., Semenov E.A. et al. // Powder Technol. 2023. V. 413. 118030. https://doi.org/10.1016/j.powtec.2022.118030
  30. Jacob K.T., Shreyas V. // J. Mater. Sci. 2017. V. 53. P. 1723. https://doi.org/10.1007/s10853-017-1634-0
  31. Kim S., Won H., Hayk N. et al. // Mater. Sci. Eng., B. 2011. V. 176. P. 1521. https://doi.org/10. 1016/j.mseb.2011.09.014
  32. Xu C.-N., Yamada H., Wang X. et al. // Appl. Phys. Lett. 2004. V. 84. P. 3040. https://doi.org/doi/10.1063/1.1705716
  33. Kozerozhets I.V., Panasyuk G.P., Semenov E.A. et al. // Russ. J. Inorg. Chem. 2020. V. 65. P. 1384. https://doi.org/10.1134/S0036023620090090

© Л.О. Козлова, Ю.В. Иони, А.Г. Сон, Г.А. Бузанов, Г.П. Муравьева, И.В. Козерожец, 2023

Согласие на обработку персональных данных с помощью сервиса «Яндекс.Метрика»

1. Я (далее – «Пользователь» или «Субъект персональных данных»), осуществляя использование сайта https://journals.rcsi.science/ (далее – «Сайт»), подтверждая свою полную дееспособность даю согласие на обработку персональных данных с использованием средств автоматизации Оператору - федеральному государственному бюджетному учреждению «Российский центр научной информации» (РЦНИ), далее – «Оператор», расположенному по адресу: 119991, г. Москва, Ленинский просп., д.32А, со следующими условиями.

2. Категории обрабатываемых данных: файлы «cookies» (куки-файлы). Файлы «cookie» – это небольшой текстовый файл, который веб-сервер может хранить в браузере Пользователя. Данные файлы веб-сервер загружает на устройство Пользователя при посещении им Сайта. При каждом следующем посещении Пользователем Сайта «cookie» файлы отправляются на Сайт Оператора. Данные файлы позволяют Сайту распознавать устройство Пользователя. Содержимое такого файла может как относиться, так и не относиться к персональным данным, в зависимости от того, содержит ли такой файл персональные данные или содержит обезличенные технические данные.

3. Цель обработки персональных данных: анализ пользовательской активности с помощью сервиса «Яндекс.Метрика».

4. Категории субъектов персональных данных: все Пользователи Сайта, которые дали согласие на обработку файлов «cookie».

5. Способы обработки: сбор, запись, систематизация, накопление, хранение, уточнение (обновление, изменение), извлечение, использование, передача (доступ, предоставление), блокирование, удаление, уничтожение персональных данных.

6. Срок обработки и хранения: до получения от Субъекта персональных данных требования о прекращении обработки/отзыва согласия.

7. Способ отзыва: заявление об отзыве в письменном виде путём его направления на адрес электронной почты Оператора: info@rcsi.science или путем письменного обращения по юридическому адресу: 119991, г. Москва, Ленинский просп., д.32А

8. Субъект персональных данных вправе запретить своему оборудованию прием этих данных или ограничить прием этих данных. При отказе от получения таких данных или при ограничении приема данных некоторые функции Сайта могут работать некорректно. Субъект персональных данных обязуется сам настроить свое оборудование таким способом, чтобы оно обеспечивало адекватный его желаниям режим работы и уровень защиты данных файлов «cookie», Оператор не предоставляет технологических и правовых консультаций на темы подобного характера.

9. Порядок уничтожения персональных данных при достижении цели их обработки или при наступлении иных законных оснований определяется Оператором в соответствии с законодательством Российской Федерации.

10. Я согласен/согласна квалифицировать в качестве своей простой электронной подписи под настоящим Согласием и под Политикой обработки персональных данных выполнение мною следующего действия на сайте: https://journals.rcsi.science/ нажатие мною на интерфейсе с текстом: «Сайт использует сервис «Яндекс.Метрика» (который использует файлы «cookie») на элемент с текстом «Принять и продолжить».