Email this article INFLUENCE OF STIRRING SPEED ON KINETIC AND MORPHOLOGICAL PARAMETERS OF GROWTH OF AMORPHOUS SILICA NANOSPHERES OBTAINED BY THE STOBER METHOD
- Authors: Yurasova I.I1, Murayeva L.N1, Ibragimov A.R1, Kuznetsov N.N1
-
Affiliations:
- Moscow State University N. E. Bauman Moscow State Technical University
- Issue: Vol 99, No 9 (2025)
- Pages: 1387-1393
- Section: PHYSICAL CHEMISTRY OF NANOCLUSTERS, SUPRAMOLECULAR STRUCTURES, AND NANOMATERIALS
- Submitted: 25.12.2025
- Published: 15.09.2025
- URL: https://ogarev-online.ru/0044-4537/article/view/362387
- DOI: https://doi.org/10.7868/S3034553725090126
- ID: 362387
Cite item
Open Access
Access granted
Subscription Access
Abstract
Calorimetric and conductometric analysis methods in online mode for the synthesis of silica globules have been used. The dependence of the initial reaction rate of sol synthesis on the stirring rate of the reaction mixture was obtained. The stirring regions corresponding to diffusive and kinetic character of synthesis at the ratio of components Si(OC2H5)4 : H2O : NH3H2O – 0.2 : 18.9 : 2.0 (mol l−1) have been revealed. The kinetic region lies in the stirring frequency range of 7–23 Hz, which is characterized by a constant process rate and quality of the grown nanospheres, and the diffusive one up to 7 Hz with varying synthesis parameters. SEM-photographs of samples with determination of average sizes and deviation of sizes at different stirring speeds were analyzed. Morphological defects of nanospheres grown in the diffusion synthesis mode have been observed.
About the authors
I. I Yurasova
Moscow State University N. E. Bauman Moscow State Technical University
Email: yurasovaii@bmstu.ru
Moscow, Russia
L. N Murayeva
Moscow State University N. E. Bauman Moscow State Technical UniversityMoscow, Russia
A. R Ibragimov
Moscow State University N. E. Bauman Moscow State Technical UniversityMoscow, Russia
N. N Kuznetsov
Moscow State University N. E. Bauman Moscow State Technical UniversityMoscow, Russia
References
- Haritha K., Henry D., Shirley J. et al. // Clinical therapeutics. 2023. V. 45. P. 1060.
- Yingze C., Wentao Zh., Xiang Zh. et al. // International Scholarly Research Notices. 2013. V. 2013. P. 745397.
- Dongming Q., Chao L., Hongting Zh. et al. // J. of Dispersion Science and Technology. 2017. V. 38. P. 70.
- Stöber W., Fink A., Bohn E. // J. of Colloid and Interface Sci. 1968. V. 26. P. 62.
- Ghimire P.P., Jaroniec M. // J. of Colloid and Interface Sci. 2021. V. 584. P. 838.
- Han Y., Ziyang L., Zhaoqiang T. // Langmuir. 2017. V. 33. P. 5879.
- Vörös-Horváth B., Salem A., Kovács B. et al. // Nanomaterials. 2024. V. 14. P. 1561.
- Bogush G., Tracy M., Zukoski I. // J. of non-crystalline solids. 1988. V. 104. P. 95.
- Giesche H. // J. of the European Ceramic Society. 1994. V. 14. P. 189.
- Fernandes R., Raimundo I., Pimentel M. // Colloids and Surfaces A. 2019. V. 577. P. 1.
- Chang Y.W., Kim W.S., Kim W.S. // Korean J. of Chem. Engineering. 1996. V. 13. P. 496.
- Gautam K.D., Ullas A.V. // Materials Today: Proceedings. 2023. V. 74. P. 713.
- Zhang S., Wang C. // Nano-Structures & Nano-Objects. 2023. V. 35. P. 100994.
- Yurasova I.I., Yurasov N.I., Plokhikh A.I. et al. // Russian J. of Physical Chemistry. 2021. V. 95. P. 1207.
- Yurasova I.I., Yurasov N.I., Galkin N.K. et al. // Russian J. of General Chemistry. 2024. V. 92. P. 2005.
- Yurasova I.I., Yurasov N.I., Veligzhanin A.A. et al. // Nanobiotechnology Reports. 2024. V. 19. P. 301.
Supplementary files