Effect of Casting Temperature on Continuously-Cast Bearing Steel GCr15 Billet Structure Formation


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Modeling is conducted for solidification and formation of a cast structure of continuously-cast blooms of steel GCr15 (Russian analog is steel ShKh15). A finite element method is used in order to model the formation of the crystal structure of continuously-cast blooms. Solidification is modelled for a bloom of steel GCr15 470 × 350 mm in cross section with different values of steel overheating above the liquidus line. Results of modeling are used for simulating continuously-cast billet macrostructure. It is shown that with a reduction in casting temperature the extent of the columnar crystal zone is reduced gradually within the structure, the extent of the skin and equiaxed zones is expanded, grain density increases gradually, and the maximum grain area and radius are significantly reduced. There are no small size fine dendritic crystals within the center of the equiaxed grain zone.

Sobre autores

Dong Xu

College of Equipment Manufacturing, Hebei University of Engineering; Advanced Science Institute, Saitama Institute of Technology

Autor responsável pela correspondência
Email: xudong_xyz@163.com
República Popular da China, Handan; Fukaya

Hongyi Liu

Technical Center, Benxi Steel Croup Corporation

Email: xudong_xyz@163.com
República Popular da China, Benxi

Cheng Peng

Technical Center, Benxi Steel Croup Corporation

Email: xudong_xyz@163.com
República Popular da China, Benxi

Zhipu Pei

Advanced Science Institute, Saitama Institute of Technology

Email: xudong_xyz@163.com
Japão, Fukaya

Shan Miao

Advanced Science Institute, Saitama Institute of Technology

Email: xudong_xyz@163.com
Japão, Fukaya

Dongying Ju

Advanced Science Institute, Saitama Institute of Technology

Email: xudong_xyz@163.com
Japão, Fukaya

Mianoyong Zhu

School of Materials and Metallurgy, Northeastern University

Email: xudong_xyz@163.com
República Popular da China, Shenyang

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Springer Science+Business Media New York, 2017