Мақаланы E-mail арқылы жіберу Study of the Effect of Trace Mg Additions on Carbides in Die Steel H13
- Авторлар: Li J.1, Li J.1, Wang L.1, Zhu Q.1
-
Мекемелер:
- State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
- Шығарылым: Том 58, № 5-6 (2016)
- Беттер: 330-334
- Бөлім: Article
- URL: https://ogarev-online.ru/0026-0673/article/view/234932
- DOI: https://doi.org/10.1007/s11041-016-0012-x
- ID: 234932
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Carbides in annealed steel H13 without magnesium and with a micro-addition of magnesium (0.0010%) are studied. Trace amounts of magnesium strengthen carbide segregation and reduce their size. Carbides phases M7C3, M6 C, and M(C, N) are detected in steel H13, and this agrees with results of thermodynamic calculations.
Авторлар туралы
Ji Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
ҚХР, Beijing
Jing Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Хат алмасуға жауапты Автор.
Email: lijing@ustb.edu.cn
ҚХР, Beijing
Liang-liang Wang
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
ҚХР, Beijing
Qin-tian Zhu
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
ҚХР, Beijing
Қосымша файлдар