Structural and magnetic features of solid-phase transformations in Mn/Bi and Bi/Mn films

Аннотация

Solid-phase transformations at different annealing temperatures in Mn/Bi (Mn on Bi) and Bi/Mn (Bi on Mn) films have been studied using X-ray diffraction, electron microscopy, and magnetic measurements. It has been shown that the synthesis of the α-MnBi phase in polycrystalline Mn/Bi films begins at a temperature of ~120°C and the Mn and Bi layers react completely at 300°C. The resulting α-MnBi(001) samples have a large perpendicular magnetic anisotropy (K_u ≃ 1.5 × 10⁷ erg/cm³) and a coercive force H > H_C ~ 3 kOe. In contrast to Mn/Bi, the ferromagnetic α-MnBi phase in Bi/Mn films is not formed even at annealing processes up to 400°C and Mn clusters are formed in a Bi melt. This asymmetry in phase transformations occurs because chemosorbed oxygen existing on the surface of the Mn film in Bi/Mn films suppresses a solid-phase reaction between Mn and Bi. The analysis of the results obtained implies the existence of new low-temperature (~120°C) structural transformation in the Mn–Bi system.