Research in the Field of Preparing Molded and Unmolded Refractories Based on High-Alumina HCBS. Part 2. Properties of Starting Components and Castings Based on Composite Composition HCBS. Study of the Initial Stage of Sintering and Mullitization1


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

The initial stages of sintering and mullite formation are studied for specimens based on HCBS of complex composition prepared by combined wet milling of high-alumina bauxite and fuzed quartz. The starting materials have a different ratio of components and solid phase particle fineness. The initial sintering stage is in the range 900 – 950°C, and mullite formation 1100 – 1150°C. In the range 1150 – 1200°C there are simultaneously both sintering and mullite formation. Depending on fineness and fuzed quartz HCBS content the maximum amount of shrinkage is 0.35 – 0.60%. An increase in firing temperature to above 1200°C is accompanied by specimen growth and an increase in porosity. Even with an insignificant level of the proportion of sintering pores (0.09 – 0.11) materials have an ultimate strength in bending of 100 – 130 MPa and open porosity of 14 – 16%.

作者简介

Yu. Pivinskii

OOO NVF Kerambet-Ogneupor

编辑信件的主要联系方式.
Email: pivinskiy@mail.ru
俄罗斯联邦, St. Petersburg

P. Dyakin

FGBOU VPO St. Petersburg State Technological University (Technical University)

Email: pivinskiy@mail.ru
俄罗斯联邦, St. Petersburg

补充文件

附件文件
动作
1. JATS XML

版权所有 © Springer Science+Business Media New York, 2016