Мақаланы E-mail арқылы жіберу A Study of the Fine Structure and Phase Composition of Magnesium Alloy VMD16 in Cast and Homogenized Conditions
- Авторлар: Volkova E.F.1, Antipov V.V.1, Zavodov A.V.1
-
Мекемелер:
- Federal State Unitary Enterprise “VIAM” (FGUP “VIAM”)
- Шығарылым: Том 61, № 3-4 (2019)
- Беттер: 143-148
- Бөлім: Magnesium Alloys
- URL: https://ogarev-online.ru/0026-0673/article/view/236570
- DOI: https://doi.org/10.1007/s11041-019-00390-6
- ID: 236570
Дәйексөз келтіру
Ашық рұқсат
Рұқсат берілді
Тек жазылушылар үшін
Аннотация
Results of a study proving formation of long-period stacking ordered (LPSO) phases in the structure of magnesium alloy VMD16 of the Mg – Zn – Zr-system are presented. It is shown that the LPSO-phases have the form of plates from 1.5 to 25 nm thick. After a homogenizing annealing, the content of Zn and Y in the LPSO-phases changes. Special features of the morphology of these phases are considered.
Авторлар туралы
E. Volkova
Federal State Unitary Enterprise “VIAM” (FGUP “VIAM”)
Хат алмасуға жауапты Автор.
Email: lab24@viam.ru
Ресей, Moscow
V. Antipov
Federal State Unitary Enterprise “VIAM” (FGUP “VIAM”)
Email: lab24@viam.ru
Ресей, Moscow
A. Zavodov
Federal State Unitary Enterprise “VIAM” (FGUP “VIAM”)
Email: lab24@viam.ru
Ресей, Moscow
Қосымша файлдар