Design of Castable Refractory Nickel Alloys with Polycrystalline Structure

Resumo

The tendencies of advancement of refractory nickel alloys with polycrystalline equiaxed structure for casting turbine blades of aircraft engines are considered. Results of design and experimental studies of a new polycrystalline refractory nickel rhenium-containing alloy VZhL22 with equiaxed crystallization are presented. It is shown that alloy VZhL22 possesses high phase stability and enhanced strength \( \left({\upsigma}_{0.2}^{20^{\circ}\mathrm{C}}=930\;\mathrm{MPa},{\upsigma}_{\mathrm{r}}^{20^{\circ}\mathrm{C}}=1060\;\mathrm{MPa}\right) \), ductility, (δ^20°C = 8%) and high-temperature strength-to-weight ratio \( \left({\upsigma}_{100}^{1000^{\circ}\mathrm{C}}/d=23.85\;\mathrm{MPa}/\mathrm{g}\cdot {\mathrm{cm}}^{-3}\right) \).